Effect of zeolite exposed to ion-exchange with ammonium chloride  on reaction of sodium and potassium hydroxides with gravel aggregate

Przemysław Czapik; Zdzisława Owsiak

2/2016 vol. 21

Effect of zeolite exposed to ion-exchange with ammonium chloride on reaction of sodium and potassium hydroxides with gravel aggregate

Przemysław Czapik ¹

Zdzisława Owsiak ¹

More details

Hide details

Politechnika Świętokrzyska w Kielcach, Katedra Technologii i Organizacji Budownictwa

Publication date: 2016-03-01

Cement Wapno Beton 21(2) 79-85 (2016)

Article (PDF)

References (28)

REFERENCES (28)

M. Handke, Krystalochemia Krzemianów, AGH, Kraków 2005.

Google Scholar

C. Karakurt, İ. B. Topçu, Effect of blended cements produced with natural zeolite and industrial by-products on alkali-silica reaction and sulfate resistance of concrete, Constr. Build. Mat. 25, 1789–1795 (2011).

Google Scholar

B. Ahmadi, M. Shekarchi, Use of natural zeolite as a supplementary cementitious material, Cem. Concr. Comp., 32, 134–141 (2010).

Google Scholar

X. Feng, N. Feng, Effect of natural zeolite on alkalisilica reaction, 12th International Conference on AlkaliAggregate Reaction in Concrete, p. 512-517, Pekin 2004.

Google Scholar

N. Feng, H. Jia, E. Chen, Study on the suppression effect of natural zeolite on expansion of concrete due to alkali-aggregate reaction, Mag. Concr. Res., 50, 17–24 (1998).

Google Scholar

Z. Owsiak, P. Czapik, Zbadanie wpływu dodatku clinoptilolitu na zmniejszenie ekspansji zapraw z kruszywem reaktywnym, Cement Wapno Beton, 81, 152-157 (2014).

Google Scholar

Z. Owsiak, P. Czapik, Ograniczenie efektów reakcji alkalia-kruszywo żwirowe w betonie przez dodatek zeolitu, Cement Wapno Beton, 80, 310-320 (2013).

Google Scholar

Q. Niu, N. Feng, Effect of modifi ed Zeolite on the expansion of alkaline silica reaction, Cem. Con. Res., 35, 1784-1788 (2005).

Google Scholar

D. M. Roy, 8th ICCC Rio de Janeiro, t. I, s. 362, Rio de Janeiro 1986.

Google Scholar

10.

R. Snellings, G. Mertens, Ö. Cizer, J. Elsen, Early hydration and pozzolanic reaction in natural zeolite blended cements: Reaction kinetics and products by in situ synchrotron X-ray powder diffraction, Cem. Con. Res., 40, 1704-1713 (2010).

Google Scholar

11.

W. Kurdowski, Chemia Cementu i Betonu, SPC, Kraków 2010.

Google Scholar

12.

C. S. Poon, L. Lam, S. C. Kou, Z. S. Lin, A study on the hydration rate of natural Zeolite blended cement pastes, Constr. Build. Mat. 13, 427-432 (1999).

Google Scholar

13.

G. Mertens, R. Snellings, K. Van Balen, B. BicerSimsir, P. Verlooy, J. Elsen, Pozzolanic reactions of common natural zeolites with lime and parameters affecting their reactivity, Cem. Con. Res., 39, 233-240 (2009).

Google Scholar

14.

S. Diamond, R. S. Barneyback, L. J. Struble, Proc. 5th Int.Conf. on Alkali-Aggregate Reaction in Concrete, s. 252/22, Cape Town 1981.

Google Scholar

15.

W. Hobbs, Infl uence of pulverized–fuel ash and granulated blastfurnace slag upon expansion caused by the alkali–silica reaction, Mag. Concr. Res., 34, 83-94 (1982).

Google Scholar

16.

G. Pei-wei, W. Sheng-xing, L. Ping-hua, W. Zhong-ru, Infl uence of composite mineral admixtures on expansion and crack due to AAR, 12th International Conference on Alkali-Aggregate Reaction in Concrete, p. 716-720, Pekin 2004.

Google Scholar

17.

N. Kantiranis, K. Sikalidis, A. Godelitsas, C. Squires, G. Papastergios, A. Filippidis, Extra-framework cation release from heulandite-type rich tuffs on exchange witch NH4 +, J. Environ. Manag., 92, 1569-1576 (2011).

Google Scholar

18.

E. Horváthová-Chmielewská, Ionenaustausch an Naturzeolithen bei Wasserbehandlungsprozessen, Forschungsanst für Wasserwirtschaft, 1996.

Google Scholar

19.

L.L. Ames Jr., Zeolitic removal of ammonium ions from agricultural and other wastewaters, 13th Pacifi c Northwest Industrial Waste Conference, p. 135, Waszyngton 1967.

Google Scholar

20.

T. Armbuster, Dehydration mechanism of clinoptilolite: Single-crystal X-ray study of Na-poor, Ca-, K-, Mg-rich clinoptilolite at 100 K Sample Dehyd 2 Data obtained from the ICSD, Am. Miner., 78, 260–264 (1993).

Google Scholar

21.

R. Pignatelli, C. Comi, P. J. M. Monteiro, A coupe mechanical and chemical damage model for concrete affected by alkali-silica reaction, Cem. Con. Res., 53, 196-210 (2013).

Google Scholar

22.

Y.-F. Wang, F. Lin, W.Q. Pang, Ammonium exchange in aqueous solution using Chinese natural clinoptilolite and modifi ed Zeolite, J. Hazard. Mater., 142, 160-164 (2007).

Google Scholar

23.

Z. Owsiak, J. Zapała, P. Czapik, Rozpoznanie przyczyn reakcji kruszywa żwirowego z alkaliami w betonie, Cement Wapno Beton, 79, 149-154 (2012).

Google Scholar

24.

M. Collepardi, J. J. Ogoumagh Olagot, Internal sulfate attack and delayed ettringite formation [w]: K. Scivener, J. Skalny, International RILEM Workshop on Internal Sulfate Attack and Delayed Ettringite Formation, Villars 2002.

Google Scholar

25.

Z. Owsiak, Alkali-aggregate reaction in concrete containing high-alkali cement and granite aggregate, Cem. Con. Res., 34, 7-11 (2004).

Google Scholar

26.

ASTM C 227 - 10 Standard Test Method for Potential Alkali Reactivity of Cement- Aggregate Combinations (Mortar-Bar Method).

Google Scholar

27.

ASTM C 1260 - 07 Standard Test Method for Potential Alkali Reactivity of Aggregates (Mortar-Bar Method).

Google Scholar

28.

PN-EN 1015-3:2000 Metody do badań zapraw murowych – część 3: Określenie konsystencji świeżej zaprawy (za pomocą stolika rozpływu).

Google Scholar

Submit your paper