Effect of graphite nanoparticles on strength and carbonation performance of cement mortar
1
School of Engineering, Fujian Jiangxia University, Fuzhou, Fujian 350108, China
Publication date: 2021-01-26
Cement Wapno Beton 25(6) 495-504 (2020)
KEYWORDS
ABSTRACT
Strength and carbonation performance are two main concerns in porous cementitious materials exposed to the atmosphere with an increasing concentration of CO2. Carbon-based reinforcers have been widely investigated in recent decades. However, practical applications have been impeded by their high cost. In this paper, inexpensive graphite nanoparticles were used to improve cement mortar. The compressive strength and carbonation performance were evaluated. XRD and SEM-EDX tests were conducted to further analyse the mechanisms. The results showed that the effects of graphite nanoparticles differed in dosage. The addition of graphite nanoparticles in the amount of 0.5% by mass significantly enhanced the performance against carbonation, while slightly worsened the compressive strength. On the contrary, 1.0% addition enhanced both the performance against CO2 penetration and strength of cement mortar after carbonation.
REFERENCES (35)
1.
J.A. Bogas,S. Real, A review on the carbonation and chloride penetration resistance of structural lightweight aggregate concrete, Mater. 12 (345620) (2019).
2.
X. Pan, C. Shi, J. Zhang, L. Jia,L. Chong, Effect of inorganic surface treatment on surface hardness and carbonation of cement-based materials, Cement Concrete Comp. 90, 218-224 (2018).
3.
G. Li, W.J. Hu, H.Y. Cui,J.C. Zhou, Long-term effectiveness of carbonation resistance of concrete treated with nano-SiO2 modified polymer coatings, Constr. Build. Mater. 201, 623-630 (2019).
4.
G. Li, H.Y. Cui, J.C. Zhou,W.J. Hu, Improvements of nano-TiO2 on the long-term chloride resistance of concrete with polymer coatings, Coatings 9 (3235) (2019).
5.
J. Li, Y.S. Ji, L.L. Zhang,B.L. Liu, Resistance to sulfate attack of magnesium phosphate cement-coated concrete, Constr. Build. Mater. 195, 156-164 (2019).
6.
M. Norhasri, M.S. Hamidah,A.M. Fadzil, Applications of using nanomaterial in concrete: a review, Constr. Build. Mater. 133, 91-97 (2017).
7.
K. Snehal, B.B. Das,M. Akanksha, Early age, hydration, mechanical and microstructure properties of nano-silica blended cementitious composites, Constr. Build. Mater. 233 (UNSP 117212) (2020).
8.
S. Haruehansapong, T. Pulngern,S. Chucheepsakul, Effect of nanosilica particle size on the water permeability, abrasion resistance, drying shrinkage, and repair work properties of cement mortar containing nano-SiO2, Adv. Mater. Sci. Eng. (4213690) (2017).
9.
O.A. Naniz,M. Mazloom, Effects of colloidal nano-silica on fresh and hardened properties of self-compacting lightweight concrete, J. Build. Eng. 20, 400-410 (2018).
10.
Y. Zhang, H.Q. Liu, R.M. Tong, J. Ren, Effect of nano silica on freeze-thaw resistance of cement-fly ash mortars, cured in corrosive condition at different temperature, CEMENT WAPNO BETON, 24, 137-143 (2019).
11.
R. Madandoust, E. Mohseni, S.Y. Mousavi,M. Namnevis, An experimental investigation on the durability of self-compacting mortar containing nano-SiO2, nano-Fe2O3 and nano-CuO, Constr. Build. Mater. 86, 44-50 (2015).
12.
K. Thangapandi, R. Anuradha, N. Archana, P. Muthuraman, O.A. Paul,R. Gobinath, Experimental study on performance of hardened concrete using nano materials, Ksce. J. Civ. Eng. 24 (2), 596-602 (2020).
13.
T. Shi, Z.X. Li, J. Guo, H. Gong,C.P. Gu, Research progress on CNTs/CNFs-modified cement-based composites, Constr. Build. Mater. 202, 290-307 (2019).
14.
A. Jamrozik, R. Wisniowski, S. Stryczek, Effect of graphene oxide on properties of cement slurries, CEMENT WAPNO BETON, 23, 59-65 (2018) .
15.
Y. Xu, J. Zeng, W. Chen, R. Jin, B. Li,Z. Pan, A holistic review of cement composites reinforced with graphene oxide, Constr. Build. Mater. 171, 291-302 (2018).
16.
W.J. Long, J.J. Wei, F. Xing,K.H. Khayat, Enhanced dynamic mechanical properties of cement paste modified with graphene oxide nanosheets and its reinforcing mechanism, Cement Concrete Comp. 93, 127-139 (2018).
17.
P. Alafogia nni, K. Dassios, C.D. Tsakiroglou, T.E. Matikas,N.M. Barkoula, Effect of cnt addition and dispersive agents on the transport properties and microstructure of cement mortars, Constr. Build. Mater. 197, 251-261 (2019).
18.
S.H. Jung, S. Oh, S.W. Kim,J.H. Moon, Effects of CNT dosages in cement composites on the mechanical properties and hydration reaction with low water-to-binder ratio, Appl. Sci-Basel. 9 (463021) (2019).
19.
X. Cui, D.C. Zhou, Y.L. Wang, B.G. Han, Properties of cement-based composites with nano-SiO2 and carbon fibers, CEMENT WAPNO BETON, 23, 317-323 (2018).
20.
J. An, B.H. Nam, Y. Alharbi, B.H. Cho,M. Khawaji, Edge-oxidized graphene oxide (EOGO) in cement composites: cement hydration and microstructure, Compos. Part B-Eng. 173 (UNSP 106795) (2019).
21.
H.J. Du,S.D. Pang, Dispersion and stability of graphene nanoplatelet in water and its influence on cement composites, Constr. Build. Mater. 167, 403-413 (2018).
22.
B. Wang,S. Deng, Effect and mechanism of graphene nanoplatelets on hydration reaction, mechanical properties and microstructure of cement composites, Constr. Build. Mater. 228 (UNSP 116720) (2019).
23.
B.M. Wang, B.L. Guo, Y. Han, Y. Zhang,Y. Li, Microstructure synthesis and characterization of carbon nanofibers reinforced cement-based composites, J. Test. Eval. 47 (6), 4379-4388 (2019).
24.
M.M. Hu, J.T. Guo, J.J. Fan, P.P. Li,D. Chen, Dispersion of triethanolamine-functionalized graphene oxide (TEA-GO) in pore solution and its influence on hydration, mechanical behavior of cement composite, Constr. Build. Mater. 216, 128-136 (2019).
25.
X.T. Qin, S.Y. Zhu, R.T. Zhang, X. He,Y. Jiang, Evaluation of stabilized graphite nanoplatelets: dispersion quality and mechanical properties of cement composites, J. Test. Eval. 47 (5), 3470-3479 (2019).
26.
H. Peng, Y.P. Ge, C.S. Cai, Y.X. Zhang,Z. Liu, Mechanical properties and microstructure of graphene oxide cement-based composites, Constr. Build. Mater. 194, 102-109 (2019).
27.
L. Zhao, X.L. Guo, Y.Y. Liu, Y.H. Zhao, Z.T. Chen, Y.S. Zhang, L.P. Guo, X. Shu,J.P. Liu, Hydration kinetics, pore structure, 3D network calcium silicate hydrate, and mechanical behavior of graphene oxide reinforced cement composites, Constr. Build. Mater. 190, 150-163 (2018).
28.
B.M. Wang,S. Deng, Effect and mechanism of graphene nanoplatelets on hydration reaction, mechanical properties and microstructure of cement composites, Constr. Build. Mater. 228 (UNSP 116720) (2019).
29.
B.M. Wang, R.Y. Zhao, Effect of graphene nano-sheets on the chloride penetration and microstructure of the cement based composite, Constr. Build. Mater. 161, 715-722 (2018).
30.
S.C. Devi,R.A. Khan, Effect of graphene oxide on mechanical and durability performance of concrete, J. Build. Eng. 27 (101007) (2020).
31.
S. Prabavathy, K. Jeyasubramanian, S. Prasanth, G.S. Hikku,R. Robert, Enhancement in behavioral properties of cement mortar cubes admixed with reduced graphene oxide, J. Build. Eng. 28 (101082) (2020).
32.
Y. Gao, H. Jing, Z. Zhou, W. Chen, M. Du,Y. Du, Reinforced impermeability of cementitious composites using graphene oxide-carbon nanotube hybrid under different water-to-cement ratios, Constr. Build. Mater. 222, 610-621 (2019).
33.
M. Tafesse,H.K. Kim, The role of carbon nanotube on hydration kinetics and shrinkage of cement composite, Compos. Part B-Eng. 169, 55-64 (2019).
34.
T. Chen,X. Gao, Effect of carbonation curing regime on strength and microstructure of portland cement paste, Journal of CO2 Utilization. 34, 74-86 (2019).
35.
J.M. Marangu, J.K. Thiong’O,J.M. Wachira, Review of carbonation resistance in hydrated cement based materials, J. Chem-NY. (8489671) (2019).
Share
RELATED ARTICLE
| ISSN: | 1425-8129 |
Całkowita kwota działania: 101 900 PLN
Kwota dofinansowania z MNiE: 85 100 PLN
Celem działania jest podniesienie poziomu technicznego obsługi Autorów i usprawnienie przepływu artykułów w procesie redakcyjnym.
Działania mające realizować powyższy cel polegać będą na:
- wprowadzeniu systemu elektronicznego zarządzania zgłaszaniem, recenzowaniem i przetwarzaniem artykułów,
- zmiana dotychczasowej organizacji strony internetowej,
- integracja numerów DOI (przydzielanych obecnie publikowanym artykułom) z bazą CrossRef.
© 2006-2024 Journal hosting platform by Bentus
We process personal data collected when visiting the website. The function of obtaining information about users and their behavior is carried out by voluntarily entered information in forms and saving cookies in end devices. Data, including cookies, are used to provide services, improve the user experience and to analyze the traffic in accordance with the Privacy policy. Data are also collected and processed by Google Analytics tool (more).
You can change cookies settings in your browser. Restricted use of cookies in the browser configuration may affect some functionalities of the website.
You can change cookies settings in your browser. Restricted use of cookies in the browser configuration may affect some functionalities of the website.